1. BLANK'S FEATURE
a. Material: KZ-3YF
b. Sintered Particles’ Size Ave≤0.3um
(By intercept measured)
Sintered particles size is very vital for bending strength at FERRULE substance.
Reportedly, that size should be controlled within 0.3um.
c. Pore-Free
The refined Binder system materialized Pore-Free.
d. Inner diameter with the few taper (less than 3um)
The few taper of the inner part is able to produce the ‘SINGLE-MODE FERRULE’ well |
| efficiency. |
| Center-Less Polishing (when the process was beginning): |
|
| SC Type can be processed fromΦ2.62±0.03 toΦ2.55±0.005. |
 |
| LC Type can be processed fromΦ1.70±0.03 toΦ1.50±0.005. |
| |
| Steel Wire Setting |
 |
| When the metal of fixation, set wire size should be chosen properly for avoid of inclination |
| Ferrule Blank’s Line as small as possible; |
Length Cutting
SC Type: 10.6~10.8mm
LC Type: 6.8~7.0mm |
 |
★Pay attention to above points, the Single-Mode Ratio will over 80%.
e. Fine Concentricity
Our Blank with fine concentricity (refer to the attached inspection data with products) can be grinded |
| 100um at a time avoid wire’s injury. |
f. Color
Pearl like white |
| |
| 2.Inspection Standard Document |
|
Inspection Item |
Standard value and range |
Measurement Instrument |
Judge standard |
|
Foreign substance |
There is no remarkable foreign substance except length parts which out of 12mm from the tip and from the end |
×1.5 of magnifier |
Spot inspectionJIS Z9015 spot qty: 32pcs/timeAQL:0. 65 L~1000Ac 1 Re 2 |
|
Coloration |
There is no remarkable coloration except length parts which out of 12mm from the tip and from the end |
×1.5 of magnifier |
|
Crack of corned part |
It is point out that defect (Absent case) |
×100of microscope, by eyes. |
Spot inspectionJIS Z9015AQL0.4 L~1000 Ac Re1 time =50 0 22 time =50 1 2When lot is NG. All qty’s of each NG. Lot must be done inspected. |
|
Outer diameter |
Φ2.62±0.03mm |
Micrometer at 5mm from the tip. |
N=2/L~1000Ac 0 Re 1 |
|
Inner diameter |
Φ0.115±0.003mm |
120μm wire should not pass into hole more than 2mm from the end part |
N=5/L~1000Ac 0 Re 1 |
|
Concentricity |
Less than 15μm |
Both hold pins type |
N=5/L~1000Ac 0 Re 1 |
|
Length |
12.80±0.5mm |
Dial caliber |
N=1/L~1000Ac 0 Re 1 | |